From: Study on mixing behaviour of aluminium-ceramic powder having high SiC volume fractions up to 50 vol.%
Siev size
> 63 µm
> 20 µm
< 20 µm
AlSi7Mg0.6 (F220)
0.3%
90.2%
9.5%
> 400 µm
> 250 µm
< 250 µm
AlSi7Mg0.6 (F60)
0.1%
96.6%
3.3%