Table 3 Morphological properties based on surface area analysis from X-ray scattering

From: Morphological, thermal, and thermomechanical properties of cellulose nanocrystals reinforced polylactide/poly [(butylene succinate)-co-adipate] blend composite foams

Sample

SpV (m2/cm3)

Q-invariant

Rg# (nm)

Radius of gyration

‹ls› (μm)

‹lp› (μm)

‹l› (μm)

‹lG› (μm)

PLA

129.4 ± 48.91

0.11 ± 0.02

9.83 ± 0.16

0.0046

0.026

0.0039

0.0040

B

120.7 ± 41.34

0.26 ± 0.03

11.88 ± 0.15

0.0050

0.028

0.0043

0.0048

B-CN3

110.1 ± 42.38

0.18 ± 0.02

11.05 ± 0.08

0.0057

0.031

0.0048

0.0045

B-CN6

101.9 ± 8.09

0.28 ± 0.01

11.02 ± 0.09

0.0068

0.032

0.0056

0.0046