Experiment No. | Layer height (mm), \( {\varvec{X}}_{1}\) | Print speed (mm/s), \( {\varvec{X}}_{2}\) | Ink concentration (%), \( {\varvec{X}}_{3}\) | Shrinkage (%) | Tensile strength (MPa) |
---|---|---|---|---|---|
1 | 0.30 | 12 | 20 | 47.80 | 2.37 |
2 | 0.25 | 15 | 15 | 59.30 | 1.68 |
3 | 0.30 | 12 | 30 | 40.00 | 2.65 |
4 | 0.35 | 15 | 15 | 67.75 | 1.55 |
5 | 0.30 | 12 | 20 | 46.90 | 2.25 |
6 | 0.35 | 9 | 25 | 47.54 | 2.49 |
7 | 0.30 | 6 | 20 | 46.50 | 2.55 |
8 | 0.30 | 12 | 20 | 44.20 | 2.45 |
9 | 0.25 | 9 | 15 | 46.75 | 2.17 |
10 | 0.35 | 9 | 15 | 53.00 | 2.00 |
11 | 0.25 | 15 | 25 | 50.70 | 2.25 |
12 | 0.30 | 12 | 20 | 47.10 | 2.19 |
13 | 0.30 | 12 | 10 | 59.96 | 1.52 |
14 | 0.30 | 12 | 20 | 48.10 | 2.21 |
15 | 0.25 | 9 | 25 | 38.50 | 2.58 |
16 | 0.20 | 12 | 20 | 43.00 | 2.23 |
17 | 0.40 | 12 | 20 | 66.20 | 1.41 |
18 | 0.30 | 12 | 20 | 50.20 | 2.15 |
19 | 0.30 | 18 | 20 | 72.50 | 1.32 |