Sample designation | Tensile Strength (MPa) | Tensile Strength increment (%) | Strain at break (%) | Modulus@ 100% (MPa) |
---|---|---|---|---|
ELV 0 | 4.7 ± 0.05 | - | 771 ± 10 | 2.6 |
ELV 6 | 4.9 ± 0.04 | 4.25 | 200 ± 12 | 4.6 |
ELV 7 | 5.2 ± 0.06 | 10.63 | 235 ± 8 | 5.2 |
ELV 8 | 5.6 ± 0.05 | 19.14 | 132 ± 10 | 5.7 |
ELV 9 | 6.0 ± 0.03 | 27.65 | 115 ± 11 | 6.0 |